Raw material of wire mesh sheet cold drawn low carbon steel wire base material can choose low carbon steel hot rolled disk bar or hot rolled smooth steel bar. The base material number and diameter of cold-drawn low carbon steel wire can be confirmed according to the rules in the table below. During the cold drawing process, the surface shrinkage rate of each drawing should not be greater than the wire mesh before cold drawing. Annealing shall not be carried out during wire drawing. If butt welding is required, the same production unit and base material of the same number should be selected. The appearance quality of wire mesh should not affect wire drawing. When the welding function is poor or brittle fracture occurs, special inspection should be carried out according to relevant standards.

Sixth, different composition (mainly from carbon, manganese, nickel, chromium to distinguish 201 and 304 stainless steel) steel carbon (C) silicon (Si) manganese (Mn) phosphorus (P) sulfur (S) chromium (Cr) nickel (Ni) molybdenum (Mo) copper (Cu)304 stainless steel is a kind of universal stainless steel material, Rust resistance is stronger than 200 series stainless steel materials, 600 degrees high temperature resistance. It has excellent stainless corrosion resistance and good intergranular corrosion resistance. It also has good corrosion resistance to alkali solution and most organic acids and inorganic acids.

Take 20cm galvanized wire for acid fog experiment, check the zinc content of galvanized wire through the balance to see whether it meets the zinc layer standard required by customers, ensure that the metal wire achieves the role of rust and corrosion prevention, and meet the service life required by customers. Galvanized iron wires must be packed in good condition, bound neatly and orderly, and bound inward to prevent scratches during transportation. The inspection standard of galvanized iron wire also includes the tensile test, which is decided according to the material of the galvanized wire order ordered by the customer, and it needs to be tested by comparing the raw material list.

Positive twist: Twist two or more pieces of wire into a double wire rope and then wrap the wire around the double wire. It’s called a positive twist cord which is a common double strand cord.

Pet carrier is generally made of high quality iron wire, low carbon steel wire, stainless steel wire welded, its characteristics are beautiful, lightweight, foldable, easy to store. Pet carrier appearance treatment is generally: cold galvanized, hot galvanized, spray, dip plastic, chrome plating, nickel plating and other methods. Pet cage is mainly used for family pet breeding and protection.

If the surface of galvanized wire is black and the galvanized layer is thin and uneven, the galvanized wire is partly because the inventory storage time is longer, but also because the production technical requirements of galvanized wire do not meet the standard and lead to the quality problems of galvanized wire. According to the use of galvanized wire is different, galvanized wire has soft and hard, then the galvanized wire used for binding requires the flexibility of galvanized wire is better, the flexibility of galvanized wire is good, and it can be easy for workers to operate.

Large roll galvanized wire can be divided into hot-dip galvanized wire and cold galvanized wire, the difference between the two lies in the way of zinc and the amount of zinc. Hot dip galvanizing is to soak steel wire in melted zinc liquid, hot dip galvanizing zinc fast, zinc layer thick rust prevention performance is very good, but the zinc is not uniform, and the surface is dark, the life of hot dip galvanizing can reach 20 years.

Post time: 08-09-22

4, when the greenhouse special electric galvanized shaft wire from the well and winding to the roll, be sure to clean up the well fluid, mud sand and other things stuck on the wire, and also coated with protective oil.

The entire steel surface is protected, and the melted zinc is easily coated evenly, whether in the interior of the pipe fitting in a depression, or in any other corner where the coating is difficult to access. The hardness of galvanized coating is greater than that of steel. The Eta layer of the upper layer of Z is only 70 DPN hardness, so it is easy to be dented by collisions. However, the hardness values of the lower layer of Zeta layer and delta layer are 179 and 211 DPN respectively, which are higher than that of the iron material of 159 DPN. Therefore, its impact resistance and wear resistance are quite good.

With the increasingly extensive use of hook mesh, the method of bridge rail is also different. The height of sidewalks or seatbelt outer railings should not be lower than 1.10 metres. The net distance between railings should not be greater than 140 mm and horizontal bar rails should not be used. The planning of the hook mesh is necessary to be safe and reliable, the bolt should be installed on the basis of the railing, its strength should meet the requirements of the standard.

Hook mesh we usually see everywhere, in fact, hook mesh is a kind of fence, like the highway, stadium fence, road fence, etc., have hook mesh. So what are the effects and advantages of the use of hook net?

Compared with galvanizing, hot-dip galvanizing has lower production cost and less environmental impact than galvanizing. Because the coating obtained is thicker, hot-dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for steel parts used in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, ocean exploration, metal structure, electric power transmission, shipbuilding and other industries.

Now it is more used in the binding of the construction industry. Compared with ordinary wire, it is also softer and has better luster. Use in daily life does not need to carry out maintenance and maintenance, saving a lot of time, but also save the cost of maintenance and maintenance. Annealed wire has good stability, good corrosion resistance, greatly prolonging the service life. There are many kinds, which can be selected according to different uses. The device for making annealed wire is simple, and the utilization rate of the device is improved. The material properties of annealed wire can meet different processing needs.

Deoxygenation of boiling steel is incomplete, oxygen content is high, phosphorus and other impurities distribution is uneven, local overspending, aging sensitivity and cold brittle sensitivity are high, hot cracking tendency is added. If unqualified electrode is used, if the content of carbon and sulfur in the weld metal is too high, cracks will occur. For example, when factories use acidic electrodes to weld Q235-A steel, the high carbon fernoganese in the electrode coating will lead to thermal cracks in the weld.

Second, composition. Model 201 is composed of 17Cr-4.5Ni-6Mn-N, which is a substitute steel for type 301 steel. Anping wire rolling cage is magnetic after cold working, used in railway cars. 304 composition of 18Cr-9Ni, is the most widely used stainless steel, heat resistant steel. Used for food production equipment, Xitong chemical equipment, nuclear energy, etc.

2) wire spacing: we all know that the smaller the wire spacing, the stronger the cage, in fact, too close is not good, too close to the dog will have a feeling of repression, we recommend that you buy wire spacing between 15-25mm, so it is not too close, and not too loose.

Galvanized iron wire is selected from excellent low carbon steel, through drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized, cooling and other processes. Galvanized iron wire should pay attention to the following points in the use process:

Post time: 16-11-22

2. Stainless steel 316 material should be used in coastal areas, which can resist corrosion of sea water.

Galvanized iron wire is widely used in construction, handicrafts, wire mesh, highway guardrail, product packaging and daily civilian and other fields.

Because the bundled galvanized wire is endowed with pre-tension, so it has the excellent characteristics of low relaxation value, small stress loss, good stability after loading, not easy to deformation, no fracture, strong elasticity, ordinary steel lines and rebar is difficult to match. The use of advanced galvanized finishing process, therefore, the use of hot-dip galvanized steel wire construction, not only good anti-corrosion performance, and beautiful generous. The product has the characteristics of smooth surface, high dimensional precision, good uniformity of zinc layer and firm adhesion.

Post time: 27-12-22

Spray hook net wholesale is the main component of hook net and frame, as for the frame is what kind of, can be customized according to requirements. Sometimes customers will purchase parts independently in order to reduce costs. In ORDER to ensure that spray hook net wholesale can be fixed on the ground, to ensure that its verticality to meet the requirements, it is necessary to hook net installation piling, fixed its guide frame, so that the installation of the net will achieve the requirements of use.

Steel wire mesh by its own unique advantages in the construction profession, reinforcement anti-crack occupation is indispensable reinforcement anti-crack data, high degree of product error is small, mesh mesh uniform, solid welding, strong acceptance, not easy to deformation, steel wire mesh in different fields have different called, in bridge engineering construction people call it soft reinforcement.

Zinc dipping time should be adjusted according to the thickness of wire diameter. The method of adjustment is to use the lead screw above the zinc pot, the length of the distance to the ceramic sinking roller. Thick wire diameter zinc dipping time should be long, fine wire diameter zinc dipping time should be short, zinc dipping length is in the range of 2~3.5m, which is also to reduce the zinc consumption of steel wire, is an aspect of maintaining the uniformity of zinc layer.