drug intermediates

Paint on the galvanized layer, the bonding force between each other has a great relationship with the baking temperature of the paint, and alkyd paint is coated after galvanized, and the adhesion is not a problem. After galvanized to do amino paint, paint adhesion is not very good. Do two bottom two surface, adhesion is good, if the two bottom two surface changed to two bottom three surface, that is, more paint, more baked once, again test adhesion is very bad, bad enough to tear the paint from the galvanized layer.

In order to pack and bind galvanized wire in the surface of the sedimentary layer to local removal of surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank. Moderate rates of foam formation may be harmless. Small, homogeneous particles of large denier present in the bath can stabilize the foam layer. Use activated carbon mat to remove surface active substance. Or through filtration to make the foam is not too stable, which are effective measures; Other measures should also be taken to reduce the amount of surfactant introduced. The electroplating speed can be obviously reduced by the addition of organic matter. Although chemical formulations facilitate high deposition rates, the deposition of organic matter does not meet the requirements of coating thickness, so activated carbon can be used to treat the bath.

There are many categories of large rolls of galvanized wire, and different categories can be applied to different scenarios. The common application of galvanized iron wire is the application of the construction industry. One is the use of binding wire. Whether it is the binding of scaffolding or reinforcement, galvanized iron wire is needed to carry out. There are also 20kg or 50kg bundles of No. 18, No. 16, No. 14, No. 12, No. 10 galvanized coils.

If not packaged, then a car of blade thorn rope can not be loaded with many pieces, but also relatively occupied places and easy to be lost in the process of transportation. Each bundle of blade barbed rope is 50 bundles. After hydraulic compression, the volume is reduced and it is more convenient to load and unload. Forklift trucks can load and unload easily. In general, when exporting, the blade thorn rope will be packaged for sale, so that the volume occupied in the container is relatively small, which can be very easy to size and place will not take up much place.

The cooling circulation system uses spray to cool the drawing die, and takes away a lot of heat generated by the drawing machine in high speed drawing in time to ensure the quality of the wire. Control drawing process parameters: drawing speed 10 ~ 12m/s; Winding tension 8 ~ 10N; Measuring length 30km; The mass fraction of lubricant is 3.5 ~ 4.5%; pH value of lubricant 7 ~ 8; Lubricant temperature 30 ~ 40℃.

This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.