In addition to these reasons, we should also pay attention to the tooling and process must be stable, and regular testing should be done to ensure the uniformity of galvanized layer.

As we all know, iron wire rust is due to contact with water and oxygen chemical reaction, therefore, how to prevent galvanized iron wire rust, first of all, in the storage of galvanized iron wire should choose ventilated dry place, avoid wet or rain leakage, in use, in addition to follow the principle of first in first out, if accidentally caused by the destruction of galvanized layer, should be coated with anti-rust paint treatment, Otherwise, it is easy to lose the protection of galvanized layer and cause galvanized iron wire rust.

If the coating roughness is not caused by the above reasons, it may be caused by impurities in the plating solution. Can take a small amount of electroplating solution, after filtration test, then take a small amount of electroplating solution, after zinc powder treatment test, check the problem is caused by solid particles or copper, lead and other foreign metal impurities. Test them one by one and it’s not hard to find the cause of the problem. Galvanized iron wire coating foaming, binding force is not good.

First, the effect of tensile strength or hardness of steel wire

Cattle fence network in outdoor use for a long time will inevitably appear rusty corrosion, this time the use of cattle fence network life depends on the maintenance of the product is not in place, we all know that cattle fence network if a long time exposed to the harsh environment, the service life will be greatly reduced. How long does a normal cattle net last?

The derusting steel parts are immersed in the melted zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to achieve the purpose of anti-corrosion. The surface of galvanized wire coating can see whether the quality of galvanized wire is good or not. If the strength of zinc attached to the wire is very poor, then this galvanized wire do not buy, because this galvanized wire must be poor galvanized wire.

Traditional barbed wire is woven into wire, with the development of the economy, the rapid rise of all walks of life, the limitations of the use of traditional barbed wire gradually exposed, such as: aquaculture, to the chicken circle a cage can not be too dense, the wire can not be too thick, woven mesh wire once the mesh over the surface of the net will become soft. We also have the solutions: 1, rolling the straight wire into a wavy shape, but still not enough to feed chickens with mesh can only stretch out the chicken beak can not feed! 2, is electric welding mesh, with the current to the longitude and latitude of the wire spot welding together, mesh do more than most is not restricted.

Post time: 16-05-22

Fence use: The use of the fence is generally one meter two to two meters a height of the impregnated welding mesh, mesh mostly 6cm, wire diameter from 2mm to 3mm.

In current market is a lot of manufacturers, that is to say, when consumer is choosing the blade thorn rope can see more manufacturers, after the contrast is that you can know what is good, can from the strength of the manufacturer, the type of product, the quality of the product and the price of the maternity leave and so on comprehensive comparison, so when the actual choice will be more easy and convenient, And the high-value blade barbed rope in the use process can also play better, so that we really know what is a good product.

Post time: 21-10-22

In the calculation process of 12*14 specifications of barbed rope, it can not be calculated according to the above calculation formula, because first of all, two specifications of raw materials are used, the thinner the wire diameter, the higher the processing cost. Generally speaking, a kilogram of 12*14 barbed rope can reach about 7.5 meters, and the ratio of warp wire to barbed rope cannot be calculated according to the traditional ratio of 7 to 3. The exact amount of stinging and use the warp need to increase after a series of professional measurement on the loss of raw materials and so on factors to calculate.

Large roll galvanized wire is processed from high quality low carbon steel wire rod. Each wire rod rolled by continuous rolling mill is not less than 200kg, but 15% of the number of plates in each batch is allowed to be composed of two, of which the weight of each rod is not less than 80kg, and 4% of the number of plates in each batch is allowed, and the mass of its single wire rod is less than 200kg, but not less than 40kg. Each rod rolled by semicontinuous mill shall not be less than 60kg, and each batch shall be allowed to have 5% disk nitrogen. The mass of the rod shall not be less than 60kg, but not less than 30kg.